Yu，Kaiping1; Lv，Yonghu1; Chen，Peng1; Hao，Huali1; Ye，Shulong1; Deng，Chengji2; Yu，Peng1

2016

World PM 2016 Congress and Exhibition

Porous SiC parts were fabricated via powder injection molding, during which the parts were consolidated using negative pressure sintering (NPS) and positive pressure sintering (PPS). Both sintering technologies successfully produce interconnected micro-size pore structures in the sintered SiC parts. Compared to the NPSed part, the SiC particles found in the PPSed part have a more uniformly-distributed particle size and better developed sintering necks, thus imparting higher mechanical properties to the porous SiC part.

第一 ; 通讯

英语

2-s2.0-85035352674

Scopus

1.Shenzhen Key Laboratory of Nanoimprint Technology,Department of Materials Science and Engineering,South University of Science and Technology of China,Shenzhen,518055,China
2.State Key Laboratory of Refractories and Metallurgy,Wuhan University of Science and Technology,Wuhan,430081,China

Yu，Kaiping,Lv，Yonghu,Chen，Peng,et al. Fabrication of open-pore SiC parts using powder injection molding[C],2016.